Brass parts with high residual tensile stress at the surface are susceptible to season cracking (i.e. spontaneous cracking occuring on exposure to atmospheric corrosion), if its zinc percentage is more than ?
Correct answer: C
Explanation
Brass with zinc content above 20% is more prone to stress corrosion cracking due to high residual tensile stresses.